Razvoj metode za ocjenu djelotvornosti višemetalnih parnofaznih inhibitora

završni rad

• Naslov (engleski): Development of method for efficiency assessment of multimetal vapour phase inhibitors
• Autor: Ema Lovrinčić
• Mentor: Sanja Martinez (mentor)
• Član povjerenstva: Sanja Martinez (predsjednik povjerenstva)
• Član povjerenstva: Helena Otmačić Ćurković (član povjerenstva)
• Član povjerenstva: Igor Sutlović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2018-09-03, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo; Kemijsko inženjerstvo u razvoju materijala

Sažetak

Parnofazni inhibitori korozije danas su jedna od najučestalijih metoda antikorozivne zaštite zbog svoje visoke djelotvornosti. Budući da broj inhibitora dostupnih na tržištu kontinuirano raste, od velike važnosti su ispitivanja provedena u laboratorijskim i realnim uvjetima kojima se određuje njihova djelotvornost i vijek trajanja. U ovom radu prikazan je razvoj metode za ocjenu djelotvornosti višemetalnih parnofaznih inhibitora na bakru uz simuliranje kloridima i jodom izazvane korozije. Tijekom ispitivanja, uzorci su bili izloženi agresivnom okolišu, a za zaštitu od korozije korišten je parnofazni inhibitor u obliku filma, VpCI-126®. Korozija je izazvana uranjanjem uzoraka u otopinu natrijeva klorida, čija se koncentracija optimirala, kako bi se ispitala djelotvornost inhibitora ovisno o koncentraciji kloridnih iona u zatvorenom sustavu. Na temelju dobivenih rezultata, provedeno je i ispitivanje u kojem se ispitala ovisnost djelotvornosti inhibitora o načinu uranjanja bakrenih uzoraka u otopinu klorida. U slučaju testiranja uzoraka jodom, korozija je izazvana injektiranjem otopine joda u zatvoreni sustav. U svakom testu uspoređivali su se uzorci zaštićeni inhibitorom sa nezaštićenim uzorcima. Uzorci su ocjenjeni vizualnim testom, snimljeni digitalnim mikroskopom, te analizirani na FTIR spektrometru. Dobiveni rezultati pokazali su da VCI ima veću djelotvornost u zatvorenim sustavima u kojima se u parnoj fazi nalazi samo voda. U prisutnosti klorida, VCI pokazuje veću djelotvornost pri niskim koncentracijama. U prisutnosti joda, vidljiv je određen stupanj zaštite kod uzoraka izloženih inhibitoru, no u usporedbi s rezultatima dobivenim u atmosferi bogatoj kloridima, inhibitor je pokazao znatno manju djelotvornost. FTIR spektri pokazali su različite promjene na površini zaštićenoj i nezaštićenoj inhibitorom.

Sažetak (engleski)

Vapour phase corrosion inhibitors are nowadays one of most common methods of anticorrosion protection because of their high efficiency. Since the number of inhibitors available on the market is constantly growing, researches done in laboratory and realistic conditions, that study their efficiency and lifespan, play a really important role. In this research work, it has been shown how the development of a method for efficiency assessment of multimetal vapour phase inhibitors works on copper with the stimulation of chlorides and iodine that cause the corrosion itself. During the testing, the samples covered in VpCl-126®, a vapour phase inhibitor in a form of a protection film, were exposed to an aggressive environment. Samples were soaked in sodium chloride solution to provoke corrosion, whose concentration was optimized, in order to test the efficiency of inhibitors depending on the concentration of chloride ions in a closed system. Because of the produced results, there were also tests with different methods of soaking copper samples in chloride solution. In a test involving iodine, corrosion is caused by injecting the iodine solution into the closed system. Samples saturated with the inhibitor were compared to the samples without inhibitor in every test. The samples were visually evaluated, photographed by a digital microscope and analyzed on FTIR spectrometer. Received results have shown that VCl has higher efficiency in closed systems in which the vapour phase contains only water. VCl shows better efficiency at low concentrations of chlorides. There is a certain level of protection on samples exposed to inhibitors in the presence of iodine. Comparing both recieved results from chloride and iodine researches, VCI has shown lower efficiency in atmosphere rich with iodine. FTIR spectra showed different kinds of changes on the surface saturated by inhibitor contrary to an surface without inhibitor.

• Ključne riječi: parnofazni inhibitor; bakar; korozija; metode ispitivanja
• Ključne riječi (engleski): vapour phase inhibitor; copper; corrosion; test methods
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:534594
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2021-06-24 09:43:45