Određivanje nestehiometrije kisika u perovskitima permanganatnom titracijom

završni rad

• Naslov (engleski): Determination of oxygen nonstoichiometry in perovskites by permanganate titration
• Autor: Valentina Jakopović
• Mentor: Jelena Macan (mentor)
• Član povjerenstva: Jelena Macan (predsjednik povjerenstva)
• Član povjerenstva: Ana Vrsalović Presečki (član povjerenstva)
• Član povjerenstva: Krunoslav Žižek (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2021-09-06, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

Za potpunu karakterizaciju manganovih perovskita, manganita, vrlo je važan parametar nestehiometrija kisika. Nestehiometrija kisika direktno je povezana s omjerom Mn3+/Mn4+ koji utječe na svojstva manganita. Perovskiti bogati kisikom imaju izraženija magnetska svojstva pri sobnoj temperaturi, dok kod onih s deficitom kisika prevladavaju električna svojstva. Postoji nekoliko metoda kojima je moguće odrediti nestehiometriju kisika u perovskitima, kao što su termogravimetrijska analiza (TGA) i volumetrijske metode (titracije). Cilj ovog rada bio je ispitati primjenjivost metode permanganatne titracije uz Mohrovu sol na određivanje nestehiometrije kisika u manganitima. Postupkom titracije određen je sadržaj kisika u uzorcima La1-xSrxMnO3 pripremljenima limunskim (x = 0, 0,1, 0,2 i 0,3) i koprecipitacijskim (x = 0, 0,1, 0,2, 0,3 i 0,5) postupkom sinteze. Utvrđeno je da je metoda permanganatne titracije primjenjiva na određivanje nestehiometrije kisika u manganitima te da ju je moguće jednostavno, brzo i ponovljivo primjenjivati. Osim toga, rezultati su pokazali da je koprecipitacijskim postupkom sinteze moguće proizvesti uzorke s izraženijom nestehiometrijom kisika za primjene u kojima je potrebna velika električna provodnost materijala.

Sažetak (engleski)

The oxygen nonstoichiometry parameter is very important for the complete characterization of manganese perovskites, manganites. Oxygen nonstoichiometry is directly related to the Mn3+/Mn4+ ratio, which in turn affects the properties of manganites. Perovskites rich in oxygen have more pronounced magnetic properties at room temperature, while those with oxygen deficiency have predominant electrical properties. There are several methods by which it is possible to determine oxygen nonstoichiometry in perovskites, such as thermogravimetric analysis (TGA) and volumetric methods (titrations). The aim of this study was to examine the applicability of the permanganate titration method with Mohr's salt for the determination of oxygen nonstoichiometry in manganites. The amount of oxygen in La1-xSrxMnO3 samples prepared by citric (x = 0, 0.1, 0.2 and 0.3) and co-precipitation (x = 0, 0.1, 0.2, 0.3 and 0.5) synthesis procedure was determined by permanganate titration. It was observed that the permanganate titration method is applicable on the oxygen nonstoichiometry determination in perovskites and that it is simple, fast and reproducible. Furthermore, the obtained results have shown that it is possible to prepare samples with high oxygen nonstoichiometry by co-precipitation procedure for applications which are requiring high electrical conductivity of the material.

• Ključne riječi: Mohrova sol; nestehiometrija kisika; permanganatna titracija; perovskiti
• Ključne riječi (engleski): Mohr's salt; oxygen nonstoichiometry; permanganate titration; perovskite
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:389112
• Projekt: Šifra: IP-2018-01-5246; Naziv: Nanokompoziti s perovskitima za fotovoltaike, fotokatalizu i senzoriku; Kratica: NanoPeroPhotoSens; Voditelj: Andreja Gajović; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: IP
• Studijski program: Naziv: Kemijsko inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2023-04-04 07:23:56