UV razgradnja PLA biokompozita ojačanih otpadom masline (drvo i lišće)

diplomski rad

• Naslov (engleski): UV degradation of PLA biocomposites reinforced with olive waste (wood andleaves)
• Autor: Helena Lončar
• Mentor: Emi Govorčin Bajsić (mentor)
• Član povjerenstva: Emi Govorčin Bajsić (predsjednik povjerenstva)
• Član povjerenstva: Ljerka Kratofil Krehula (član povjerenstva)
• Član povjerenstva: Mirela Leskovac (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2024-09-25, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

U svrhu ovog rada provedena je UV razgradnja biokompozita proizvedenih od poli(mliječne kiseline) (PLA) s dodatkom otpada masline u različitim udjelima (2,5%, 5%, 7,5% i 10 mas.%), bez i s dodatkom plastifikatora trietil citrata (TEC) u udjelu od 20 mas.%. Cilj je istražiti utjecaj UV zračenja na svojstva PLA biokompozita koji se mogu koristiti kao ambalažni materijali zbog njihove zdravstvene i ekološke sigurnosti. Svi uzorci su podvrgnuti UV razgradnji tijekom 720h. Promjene u strukturi nakon UV zračenja praćene su Infracrvenom spektroskopijom s Fourierovom transformacijom (FTIR) dok su toplinska svojstva određena diferencijalnom pretražnom kalorimetrijom (DSC). Rezultati su pokazali da UV razgradnja utječe na kemijsku i toplinsku stabilnost biokompozita, što ima značajan utjecaj na njihovu dugovječnost i primjenjivost kao ambalažnog materijala.

Sažetak (engleski)

This study investigated the UV degradation of biocomposites made from poly(lactic acid) (PLA) with the addition of olive waste at various content (2.5%, 5%, 7.5%, and 10 wt.%), withouth and with the addition of the plasticizer triethyl citrate (TEC) at a concentration of
20 wt%. The aim was to investigated the effect of UV irradiation on the properties of PLA biocomposites that can be used as a packaging material due to their health and environmental safety. All samples were subjected to UV degradation over a period of 720h to examine the changes caused by photodegradation. Measurements were conducted using Fourier Transform Infrared Spectroscopy (FTIR) to investigate structural changes induced by UV irradiation, and Differential Scanning Calorimetry (DSC) to determine thermal properties. The results indicated that UV degradation affects the chemical and thermal stability of the biocomposites, which has a significant impact on their longevity and suitability as packaging materials.

• Ključne riječi: biokompoziti; poli(mliječna kiselina); UV zračenje; fotooksidacija
• Ključne riječi (engleski): biocomposites; poly(lactid acid); UV irraddiation; photooxidation
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:558630
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra inženjer/inženjerka kemijskog inženjerstva (univ. mag. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2024-11-06 13:59:50