Utjecaj soli zemnoalkalijskih metala na portland cement

diplomski rad

• Naslov (engleski): Influence of earth alkali metal salts on portland cement
• Autor: Silvia Dratibi
• Mentor: Nevenka Vrbos (mentor)
• Član povjerenstva: Nevenka Vrbos (predsjednik povjerenstva)
• Član povjerenstva: Emi Govorčin Bajsić (član povjerenstva)
• Član povjerenstva: Juraj Šipušić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2021-09-20, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

Kako bi se odredio utjecaj klorida zemnoalkalijskih metala (CaCl2∙2H2O, MgCl2∙6H2O, SrCl2∙6H2O) na svojstva modificiranog hidrauličnog veziva, pripremljeni su uzorci portland cementa PC sa dodatkom ispitivanih soli u masenim udjelima od 1-5 % na masu cementa. Pripravljeni uzorci karakterizirani su mjerenjem vremena vezanja, čvrstoće na tlak i brzine razvoja topline hidratacije. Vrijeme vezanja pripravljenog materijala određeno je Vicatovim aparatom. Čvrstoća na tlak mjerena je na laboratorijskoj hidrauličnoj preši nakon 24 sata, 3 dana, 7 dana i 28 dana hidratacije u bazenima s vodom. Toplina hidratacije mjerena je u kalorimetru tijekom 60 sati. Uzorci sa 1, 2 i 5 % dodane zemnoalkalijske soli ispitani su rendgenskom difrakcijskom analizom (XRD) i karakterizirani su infracrvenom spektrometrijom s Fourirerovom transformacijom (FTIR). Provedena mjerenja pokazala su smanjenje vremena vezanja i čvrstoće na tlak s povećanjem udjela soli, a brzina razvoja topline hidratacije povećala se povećanjem udjela CaCl2∙2H2O i SrCl2∙6H2O. Povećanje udjela MgCl2∙6H2O nije značajnije utjecalo na brzinu reakcije hidratacije.

Sažetak (engleski)

In order to investigate the influence of earth alkaline chlorides (CaCl2∙2H2O, MgCl2∙6H2O, SrCl2∙6H2O) on modified hydraulic binder's properties, samples of portland cement with 1-5 % additions of stated salts were prepared. Setting time, compressive strength and heat of hydration were measured. Setting time of the samples was measured on Vicat apparatus. Compressive strength was measured with laboratory hydraulic press after 24 hours, 3 days, 7 days and 28 days of hydration in water tank. Calorimeter was used to measure the heat development during 60 hours. Samples with 1 %, 2 % and 5 % additions were characterized by X-ray diffractometry (XRD) and Fourier transform infrared spectroscopy (FTIR). The analysis showed the acceleration of the setting time and deterioration of compressive strength for higher salt concentrations. Heat of hydration increased with the addition of CaCl2∙2H2O and SrCl2∙6H2O. The addition of MgCl2∙6H2O did not affect the hydration rate.

• Ključne riječi: portland cement; zemnoalkalijske soli; vrijeme vezanja; čvrstoća; toplina hidratacije
• Ključne riječi (engleski): portland cement; alkaline earth metal salts; setting time; strength; heat of hydration
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:751401
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka kemijskog inženjerstva (mag. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-04-14 11:07:52