Priprava polimernih kompozita umrežavanjem epoksidne smole s oksidnim nano i mikročesticama

završni rad

• Naslov (engleski): Preparation of polyepoxide nanocomposite with oxide nano and micro fillers
• Autor: Blanka Gabrić
• Mentor: Ante Jukić (mentor)
• Mentor: Fabio Faraguna (komentor)
• Član povjerenstva: Ante Jukić (predsjednik povjerenstva)
• Član povjerenstva: Fabio Faraguna (član povjerenstva)
• Član povjerenstva: Zvonimir Katančić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2020-09-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Temeljne tehničke znanosti

Sažetak

Cilj ovog rada je priprava i karakterizacija polimernih kompozita koji će pokazati poboljšane vrijednosti toplinske vodljivosti u odnosu na polazni polimer. Kao polimerna matrica poslužila je epoksidna smola koja je umreživana s 2 % inicijatora i dodana su joj različita mikro i nanopunila u masenim udjelima od 0,5; 2; 5 i 20 %. Mjerene su i uspoređivane toplinske vodljivosti dobivenih kompozitnih materijala (za različite udjele punila) s uzorcima umrežene epoksidne smole. Termogravimetrijska analiza provedena je na uzorcima smole umrežene s različitim postotcima inicijatora, na uzorku za koji se pretpostavljalo da je ostvarena homogena raspodjela punila (punilo D) te na uzorku gdje je došlo do raslojavanja punila (punilo E). Kod uzoraka čistog polimera cilj je bio otkriti koliki postotak dodanog inicijatora ostvaruje najveći stupanj umreženja. Rezultati mjerenja toplinske vodljivosti pokazuju kontinuiran trend rasta za punilo A (mikropunilo) te za punila E i D (nanopunila). Rezultati termogravimetrijske analize upućuju na to da je raspodjela u slučaju kompozita s punilom D homogena dok je punilo E unutar kompozitnog materijala neravnomjerno raspodijeljeno. Za epoksidna smola/punilo A kompozit potrebno je napraviti dodatne analize kako bi se utvrdila dispergiranost punila.

Sažetak (engleski)

The aim of this work is the preparation and characterization of polymer composites that will show improved thermal conductivity values in relation to the starting polymer. The polymer matrix was an epoxy resin which was crosslinked with 2 % initiatior and various micro an nanofillers were added in mass fractions of 0.5; 2; 5; and 20 %. The thermal condutivity of the obtained composite materials (for different filler frations) were measured and compared with crosslinked epoxy resin samples. Thermogravimetric analysis was performed on samples of epoxy resin crosslinked with different percentages of initiator, on a sample that was assumed to have a homogeneous distribution of filler (composite with filler D) and on a sample where filler stratifiation occured (composite with filler E). In the case of pure polymer samples, the aim was to find out what percentage of the added initiator achieves the highest degree of crosslinking. The results of thermal conutivity measurements show a continuos growth for filler A (mirofiller) and for fillers E and D (nanofillers). The results of the thermogravimetric analysis suggest that the distribution in the case of composites with filler D is homogeneous while the filler E within the composite material is unevenly distributed. For epoxy resin/ filler A composite, additional analyses need to be performed to determine the dispersion of the filler.

• Ključne riječi: epoksidna smola; polimerni kompoziti; nanopunila; mikropunila; toplinska vodljivost
• Ključne riječi (engleski): epoxy resin; polymer composites; nanofillers; microfillers; thermal conductivity
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:263546
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-05-03 13:22:19