Utjecaj UV zračenja na LDPE/PCL mješavine

završni rad

• Naslov (engleski): The effect of UV irradiation on LDPE/PCL blends
• Autor: Paula Santini
• Mentor: Emi Govorčin Bajsić (mentor)
• Član povjerenstva: Emi Govorčin Bajsić (predsjednik povjerenstva)
• Član povjerenstva: Igor Sutlović (član povjerenstva)
• Član povjerenstva: Ljerka Kratofil Krehula (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2016-09-19, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo; Kemijsko inženjerstvo u razvoju materijala

Sažetak

Upotreba nerazgradivih polimera kao ambalažnog materijala ima loš utjecaj na okoliš. Štetno djeluju na biljni i životinjski svijet pa se uz kisele kiše, globalno zatopljenje, nestanak biljnih i životinjskih vrsta, plodnog tla i ozonskog omotača smatraju jednim od najvećih ekoloških problema današnjice. Folije polietilena niske gustoće (LDPE) primjenjuju se u pakiranju hrane zbog dobrih mehaničkih svojstava, dobre prerade te fleksibilnosti. Međutim nedostatak LDPE-a kao nerazgradivog ambalažnog materijala je veliki utjecaj na onečišćenje okoliša. U ovom radu je istražen utjecaj UV zračenja na toplinska svojstva LDPE/PCL mješavina. Mješavine polietilena niske gustoće (LDPE) i poli (ε-kaprolaktona) (PCL), (LDPE/PCL mješavine), su pripremljene iz taljevine umješavanjem LDPE i PCL u različitim omjerima (90/10, 70/30, 50/50, 30/70, 10/90 mas %) u Brabender gnjetilici. Uzorci čistih polimera i LDPE/PCL mješavina dobiveni su prešanjem u kalupu na hidrauličkoj preši. Uzorci su zračeni djelovanjem UV svjetla 30 dana. Promjene nastale fotooksidativnom razgradnjom praćene su primjenom tehnike diferencijalne pretražne kalorimetrije (DSC) i dinamičko mehaničke analize (DMA). DMA i DSC rezultati pokazuju da dolazi do porasta temperature staklastog prijelaza i kristalnosti nakon UV zračenja. Rezultati pokazuju da nakon UV zračenja dolazi do pucanja lanca i umreženja u LDPE/PCL mješavinama. Nakon zračenja u LDPE je dominantno pucanje lanca dok je kod PCL umreživanje.

Sažetak (engleski)

Nondegradable polymers as a packaging materials has bad influence on the environment, cause damage to plants, animals and along with acid rains, global warming, disappearance of plant and animal species, fertility of the soil, ozone layer it's being consider as one of the greatest environmental problem today. Low-density polyethylene (LDPE) sheets are used in food packaging because of it's good mechanical properties, easy processing and flexibility. However, the lack of LDPE as nodegradable packaging material is huge environmental pollution. In this work, the effect of ultraviolet irradiation on the thermal properties of LDPE/ PCL blends was studied. Blends of low-density polyethylene (LDPE) and poly (ε-caprolactone) (PCL), (LDPE/PCL blends) investigated were prepared with melt mixing (compounding) in Brabender mixer under different LDPE/ PCL content (90/10, 70/30, 50/50, 30/70, 10/90 wt%). The samples of the neat polymers and LDPE/PCL blends were molded in hydraulic press. The samples was exposed to UV irradiation for 30 days. The photodegradation behaviour at the exposed surfaces of LDPE / PCL blends was studied using differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) techniques. The DMA and DSC studies showed that the glass trasition and crystalinity of the LDPE in blends were increased after UV irradiation. The experimental results after UV irradiation showed that LDPE/ PCL blends undergoes both chain scission and crosslinking reactions. Chain scission reactions occurred in LDPE and for PCL crosslinking reactions predominated.

• Ključne riječi: polietilen niske gustoće (LDPE); polikaprolakton (PCL); polimerne mješavine; UV zračenje; fotooksidacija
• Ključne riječi (engleski): low-density polyethylene (LDPE); polycaprolactone (PCL); polymer blends; UV irradiation; photooxidation
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:489610
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2018-02-07 09:59:43