Sinteza i karakterizacija nanočestica srebra pogodnih za ispis tintnim pisačem

disertacija

• Naslov (engleski): Synthesis and characterization of silver nanoparticles suitable for printing using ink-jet technology
• Autor: Irena Ivanišević
• Mentor: Stjepan Milardović (mentor)
• Član povjerenstva: Danijela Ašperger (predsjednik povjerenstva)
• Član povjerenstva: Petar Kassal (član povjerenstva)
• Član povjerenstva: Dubravka Matković-Čalogović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2020-10-26, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija; Anorganska kemija
• Univerzalna decimalna klasifikacija (UDC): 54 - Kemija. Kristalografija. Mineralogija ; 620 - Ispitivanje materijala. Elektrane. Ekonomika energije

Sažetak

Drastična promjena omjera površine i veličine čestice rezultira drugačijim fizikalnim i kemijskim svojstvima nanomaterijala u odnosu na makromaterijal. Među različitim vrstama dostupnih nanomaterijala dominiraju nanočestice srebra, čija iznimna opto-elektronička i fizikalno-kemijska svojstva omogućuju njihovu svestranu primjenu. Ovdje se posebno ističe ispis vodljive nanosuspenzije tintnom tehnologijom u svrhu izrade fleksibilne elektronike. U ovom radu razvijen je brz, jednostavan i ekonomičan sintetski put priprave nanočestica srebra, zajedno s jedinstvenom metodom karakterizacije koloidne nanosuspenzije. Ciklička voltametrija korištena je kao glavna tehnika za proučavanje dosega pretvorbe ionskog u nanometalno srebro, interakcije među nanočesticama te utjecaja organskih i anorganskih kiselina na površinski vezan stabilizator. Priređene nanočestice srebra, dobivene redukcijom srebrovih(I) iona hidrazinom uz stabilizaciju poli(akrilnom kiselinom) i poli(metakrilnom kiselinom), korištene su kao ishodni materijal za pripravu vodljive tinte namijenjene tehnologiji tintnog ispisa. Za postizanje kompatibilnosti tinte i tiskarskog sustava određena su optimalna fizikalna i kemijska svojstva formulacije (viskoznost i površinska napetost), kao i oblik kristalita, raspodjela veličine čestica te njihov površinski naboj. U svrhu priprave funkcionalnog materijala zadovoljavajućih električnih značajki za primjenu u fleksibilnoj elektronici, tinte su ispisane na komercijalnim polimernim podlogama koje omogućuju hladno sinteriranje. Kombiniranim mehanizmom kemijskog i termalnog sinteriranja vodljivost ispisanih metalnih slojeva dosegla je vrijednost 70 % vodljivosti elementarnog srebra. Ove izvrsne električne značajke dokaz su optimalne izvedbe i pouzdanog ispisa suspenzije nanometalnog srebra. Na temelju dobivenih rezultata zaključeno je da priređene nanočestice srebra predstavljaju jedinstven multifunkcionalan materijal, s dokazanim potencijalom za dizajn, pripravu i karakterizaciju kemijskih (bio)senzora temeljenih na priređenim srebrovim elektrodama.

Sažetak (engleski)

As a result of the decrement in surface to volume ratio, nanomaterials have completely new physical and chemical properties, which differ from their macrosized counterparts. Compared to other nanomaterials, silver nanoparticles exhibit superior opto-electronic and physico-chemical properties, which makes them valuable materials for versatile applications. Amongst potential applications, ink-jet printing of conductive inks for the purpose of flexible electronics fabrication is of special interest. In this dissertation, a fast, simple and economical synthetic route for the preparation of silver nanoparticles has been developed, together with a unique method for the characterization of colloidal nanosuspensions. Cyclic voltammetry was used as the main technique to study the extent of ionic to nanometallic silver conversion, interactions between nanoparticles and the influence of organic and inorganic acids on the surface-bound stabilizer. The prepared silver nanoparticles, obtained by reduction of silver(I) ions with hydrazine, utilizing poly(acrylic acid) and poly(methacrylic acid) as stabilizers, were used as a base for the preparation of conductive inks suitable for ink-jet printing. To achieve compatibility of the ink and printing system, optimal physical and chemical properties of the formulation (viscosity and surface tension) were determined, as well as the shape of the crystallites, the particle size distribution and their surface charge. In order to prepare a functional material with satisfactory electrical properties for use in flexible electronics, the inks were printed onto commercial polymer substrates that allow sintering at room temperature. With the combination of chemical and thermal sintering techniques, the resultant conductivity of printed nanosilver layers reached 70% of bulk silver conductivity. These excellent electrical features are proof of the optimal and reliable printing performance of the nanometallic silver suspension. Based on the obtained results, it was concluded that the prepared silver nanoparticles represent a unique multifunctional material, with proven potential for design, preparation and characterization of chemical (bio)sensors based on the prepared silver electrodes.

• Ključne riječi: nanočestice srebra; vodljiva tinta; ciklička voltametrija; tehnologija tintnog ispisa; fleksibilna elektronika
• Ključne riječi (engleski): silver nanoparticles; conductive ink; cyclic voltammetry; ink-jet printing technology; flexible electronics
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:395205
• Datum promocije: 2020
• Studijski program: Naziv: Kemijsko inženjerstvo i primijenjena kemija; Vrsta studija: sveučilišni; Stupanj studija: poslijediplomski doktorski; Akademski / stručni naziv: doktor/doktorica znanosti, područje prirodnih znanosti, polje kemija (dr. sc.)
• Vrsta resursa: Tekst
• Opseg: 150 str. ; 30 cm
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2020-10-26
• Datum i vrijeme pohrane: 2023-06-05 09:51:16