Priprema biorazgradljivih kompozita na osnovi LLDPE i rižinih ljuskica

završni rad

• Naslov (engleski): Preparation of biodegradable composites based on LLDPE and rice husks
• Autor: Martin Cvetić
• Mentor: Emi Govorčin Bajsić (mentor)
• Član povjerenstva: Emi Govorčin Bajsić (predsjednik povjerenstva)
• Član povjerenstva: Ljerka Kratofil Krehula (član povjerenstva)
• Član povjerenstva: Veljko Filipan (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2018-09-21, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo; Kemijsko inženjerstvo u razvoju materijala

Sažetak

Sve se više dovodi u pitanje problem vezan uz odlaganje plastičnog otpada, a znanstvenici nastoje pronaći adekvatno rješenje s ciljem boljeg očuvanja i zaštite okoliša. U ovom eksperimentalnom radu pripravljeni su biokompoziti na osnovi LLDPE i rižinih ljuskica (RLJ) u svrhu dobivanja ambalažnog materijala. Biokompoziti su pripravljeni u Brabender gnjetilici dodatkom rižinih ljuskica u LLDPE u različitom masenom postotku (10, 20, 30, 40, 50 mas %). Uzorcima je ispitana toplinska stabilnost TGA tehnikom s obzirom na dodatak RLJ i njihovog udjela u bikompozitu LLDPE / RLJ. DSC tehnikom određeni su fazni prijelazi, dok su dinamičko mehaničkom analizom (DMA) određene primarne viskoelastične funkcije (modul pohrane (E'), modul gubitka (E'')). Na osnovi dobivenih rezultata može se zaključiti kako dodatkom i povećanjem udjela RLJ u biokompozitu stupanj kristalnosti raste kod manjeg udjela RLJ (10, 20 mas %) gdje RLJ djeluju kao nukleacijski agens, no povećanjem udjela RLJ (30, 40, 50 mas %) stupanj kristalnosti opada, a u tom slučaju sadržaj silike iz RLJ narušava kristalnu strukturu. Povećanjem udjela RLJ u biokompozitu bilježi se pad toplinske stabilnosti materijala što se očituje u temperaturi početka razgradnje (Tp) koja poprima niže vrijednosti što znači da do razgradnje dolazi pri nižim temperaturama. Rezultati dobiveni DMA analizom ukazuju na sniženje staklišta (Tg) dodatkom RLJ što znači da ne dolazi do uspostavljanja interakcija između LLDPE i RLJ.

Sažetak (engleski)

The question of disposal of plastic waste is increasingly questioned, and scientists are trying to find an adequate solution for better conservation and environmental protection. In this experimental work biocomposites based on LLDPE and rice husk (RH) were prepared for the purpose of obtaining packaging material. Biocomposites were prepared by laboratory Brabender mixer by adding rice husks in LLDPE with different content of rice husk (10, 20, 30, 40, 50 wt %). The samples was examined to the thermal stability with TGA technique with respect to the addition of RH and their proportion in LLDPE / RH biocoposite. By DSC techniques was obtained phase transitions, while by dynamic mechanical analysis (DMA) was determined primary viscoelastic functions (storage modulus (E'), loss modulus (E'')). Based on the obtained results, it can be concluded that by adding and increasing the RH content in biocomposites, the degree of crystallinity increases for the biocomposites with a smaller content of rice flakes (10, 20 wt %) where RH acts as nucleation agents but if the content of rice husk become higher (30, 40, 50 wt %) , the crystallinity decreases, and in that case the silica from the rice husks disrupts the crystal structure. The results obtained by DMA analysis show a decrease of glass transition temperature by the addition of RH meaning that there is no interaction between LLDPE and RH.

• Ključne riječi: biokompozit; zbrinjavanje otpada; linearni polietilen niske gustoće (LLDPE); rižine ljuskice (RLJ); svojstva biokompozita
• Ključne riječi (engleski): biocomposite; waste disposal; linear low density polyethylene (LLDPE); rice husks (RH); properties of biocomposites
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:588557
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2022-07-08 13:38:07