Sinteza nanoštapića bakrova(II) oksida

završni rad

• Naslov (engleski): Synthesis of copper(II) oxide nanorods
• Autor: Ivan Borić
• Mentor: Stanislav Kurajica (mentor)
• Član povjerenstva: Stanislav Kurajica (predsjednik povjerenstva)
• Član povjerenstva: Marija Vuković Domanovac (član povjerenstva)
• Član povjerenstva: Katarina Mužina (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2023-09-21, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

U ovom radu pripravljene su i karakterizirane nanočestice bakrova(II) oksida. Sinteza nanočesticca bakrova(II) oksida provedena je sonokemijskom metodom. Kako bi se dobio uvid u sastav i svojstva dobivenog uzorka, uzorak je podvrgnut brojnim analizama. Kristalna struktura i veličina kristalita određene su rendgenskom difrakcijskom analizom, uzorak je analiziran i infracrvenom spektroskopijom s Fourierovom transformacijom, termogravimetrijskom analizom, pretražnom elektronskom mikroskopijom, energijski disperzivnom rendgenskom spektroskopijom, a veličina i oblik čestica istraženi su mikroskopom atomskih sila. Potvrđeno je postojanje jedne faze u uzorku, bakrova(II) oksida, s kristalitima veličine do 20 nm. TGA analiza pokazala da je u uzorku prisutna i organska faza. Između 800 i 1000 °C dolazi do gubitka gotovo 10 % mase uzorka zbog pretvorbe bakrova(II) oksida u bakrov(I) oksid. Morfologija uzorka može se opisat kao homogeni pahuljasti aglomerati CuO nanočestica. Antimikrobna svojstva nanočestica bakrova(II) oksida određena su na bakterijama Pseudomonas aeruginosa i Bacillus subtilis nakon 24 h, te na gljivicama Candida albicans i Aspergillus niger nakon 72 h određivanjem zone inhibicije.

Sažetak (engleski)

In this work, copper(II) oxide nanoparticles were prepared and characterized. Synthesis of copper(II) oxide nanoparticles as accomplished using the sonochemical method. In order to gain insight into the composition and properties of the obtained sample, the sample was subjected to various analyses. The crystal structure and size of the crystallites were determined by X-ray diffraction analysis, the sample was also analyzed by infrared spectroscopy with Fourier transformation, thermogravimetric analysis, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and the size and shape of the particles were investigated with atomic force microscopy. The existence of one phase in the sample, identified as copper(II) oxide, with crystallite size up to 20 nm as confirmed. TGA analysis showed that a small part of precursor organic phase is present in the sample. Almost 10 % of the mass of the sample is lost to the chemical transformation of copper(II) oxide to
copper(I) oxide between 800 and 1000 °C. The morphology of the sample consists of homogeneously distributed fluffy-looking agglomerates of CuO nanoparticles. Antimicrobial properties of copper(II) oxide nanoparticles were determined on the bacteria Pseudomonas aeruginosa and Bacillus subtilis after 24 h, and on the fungi Candida albicans and Aspergillus niger after 72 h.

• Ključne riječi: nanočestice; bakrov(II) oksid; sonokemijska sinteza
• Ključne riječi (engleski): nanoparticles; copper(II) oxide; sonochemical synthesis
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:767910
• Studijski program: Naziv: Kemijsko inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: prijediplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2023-11-29 14:31:01