Utjecaj UV zračenja na strukturu polimera

završni rad

• Naslov (engleski): Influence of UV irradiation on polymer structure
• Autor: Lorena Bartulović
• Mentor: Zlata Hrnjak-Murgić (mentor)
• Član povjerenstva: Zlata Hrnjak-Murgić (predsjednik povjerenstva)
• Član povjerenstva: Emi Govorčin Bajsić (član povjerenstva)
• Član povjerenstva: Marijana Kraljić Roković (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2023-09-21, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

Pod utjecajem atmosferskih uvjeta, ultraljubičastog zračenja (eng. ultraviolet – UV) i topline, polimerni materijali degradiraju pri čemu dolazi do promjene njihovih svojstava kao što je na primjer povećanje krtosti i lomljivosti što za posljedicu daje nastajanje mikroplastike u okolišu. U svrhu izrade ovog rada korišteni su materijali polietilen visoke gustoće (HDPE) i polipropilen (PP) koji su izloženi atmosferskom starenju. Uzorci HDPE folija i PP folija su izloženi procesu starenja u razdoblju od 14, 28, 42 i 530 dana. Nakon tog vremenskog razdoblja, promjene koje su se dogodile uslijed procesa degradacije praćene su pomoću infracrvene spektroskopije s Fourierovom transformacijom (eng. Fourier-transform infrared spectroscopy, FTIR). Pomoću FTIR spektara identificirana je pojava razradnih skupina (karboksilne, karbonilne te oksi skupine) koje su nastale kao posljedica razgradnje polimera. Intenzitet razgradnje okarakteriziran je za određivanje karbonilnog indeksa (C.I.).
Rezultati dobiveni primjenom metode infracrvene spektroskopije pokazuju da povećanjem vremena starenja dolazi do promjene strukture molekula polimera, što je vidljivo iz povećanja karbonilnog indeksa.

Sažetak (engleski)

Under the influence of atmospheric conditions, ultraviolet (UV) radiation and heat, polymer materials undergo degradation, leading to changes in their properties such as increased brittleness and fragility, resulting in accumulation of microplastic in the environment. In this study, high-density polyethylene (HDPE) and polypropylene (PP) materials were used and were exposed to atmospheric aging. Samples of HDPE film and PP film were subjected to aging for periods of 14, 28, 42 and 530 days. After this period of time, the changes that occurred due to degradation processes were monitored using Fourier-transform infrared spectroscopy (FTIR). The FTIR spectra were utilized to identify the presence of newly formed groups (carboxyl, carbonyl and oxy groups) as a result of polymer degradation. The degree of degradation was determinated by carbonyl index (C.I.). The results of FTIR spectroscopy show that with increasing aging time, changes in the molecular structure of the polymer can be observed, which are reflected in an increased carbonyl index.

• Ključne riječi: polipropilen; polietilen visoke gustoće; UV zračenje; razgradnja; mikroplastika
• Ključne riječi (engleski): polypropylene; high-density polyethylene; UV radiation; degradation; microplastics
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:043611
• Projekt: Šifra: IP-2020-02-6033; Naziv: Mikroplastika u vodi; sudbina, ponašanje i uklanjanje; Naziv: Microplastics in water; fate and behavior and removal; Kratica: ReMiCRO; Voditelj: Ana Lončarić Božić; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: IP
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: prijediplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2023-11-29 17:00:31