Sinteza različitih ugljikovih nanostruktura kontrolom parametara depozicije metodom ablacije iskre

diplomski rad

• Naslov (engleski): Synthesis of different carbon nanostructures by controlling the deposition parameters using the spark ablation method
• Autor: Nensi Gugić
• Mentor: Vilko Mandić (mentor)
• Član povjerenstva: Vilko Mandić (predsjednik povjerenstva)
• Član povjerenstva: Mirela Leskovac (član povjerenstva)
• Član povjerenstva: Luka Pavić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2024-02-23, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo

Sažetak

Ablacija iskrom postaje sve popularnija tehnika za sintezu ugljikovih nanostruktura zbog niza prednosti koje pruža, uključujući jednostavnost, ekonomičnost te visoku kontrolu procesa proizvodnje. Ova tehnika, koja se temelji na aerosolnoj ablaciji materijala u prisutnosti inertnog plina, omogućuje dobivanje raznovrsnih ugljikovih nanostruktura kontrolom parametara depozicije. U okviru ovog rada, provedena je sinteza dva uzorka ugljikovih nanostruktura, pri čemu je jedini promjenjivi parametar bio odabir vrste plina prisutnog tijekom procesa ablacije. Prvi uzorak sintetiziran je u atmosferi argona, dok je drugi uzorak sintetiziran u atmosferi dušika. Nakon sinteze, dobiveni uzorci detaljno su karakterizirani primjenom metoda analize površinskih svojstava kao što su AFM (eng. Atomic Force Microscopy), SEM (eng. Scanning Electron Microscopy) i BET (Brunauer-Emmett-Teller) analiza.

Sažetak (engleski)

Spark ablation is becoming an increasingly popular technique for synthesis carbon nanostructures due to a range of advantages it offers, including simplicity, cost-effectiveness, and high control over the production process. This technique, based on aerosol ablation of materials in the presence of an inert gas, enables the production of diverse carbon nanostructures by controlling deposition parameters. In the context of this study, synthesis of two samples of carbon nanostructures was conducted, where the only variable parameter was selection of the gas type during the ablation process. The first sample was synthesized in an argon atmosphere, while the second sample was synthesized in a nitrogen atmosphere. After the synthesis, the obtained samples were thoroughly characterized using surface analysis methods such as AFM (Atomic Force Microscopy), SEM (Scanning Electron Microscopy), and BET (Brunauer-Emmett-Teller) analysis.

• Ključne riječi: ablacija iskrom; ugljikove nanostrukture
• Ključne riječi (engleski): spark ablation; carbon nanostructures
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:355229
• Studijski program: Naziv: Kemijsko inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra inženjer/inženjerka kemijskog inženjerstva (univ. mag. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2024-02-29 10:06:06