Sinteza i inkjet ispis amfifilnih nanočestica srebra

diplomski rad

• Naslov (engleski): Synthesis and inkjet printing of amphiphilic silver nanoparticles
• Autor: Iva Gudan Pavlović
• Mentor: Petar Kassal (mentor)
• Član povjerenstva: Petar Kassal (predsjednik povjerenstva)
• Član povjerenstva: Zvonimir Katančić (član povjerenstva)
• Član povjerenstva: Igor Dejanović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2021-09-29, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Cilj rada je priprema i inkjet ispis vodljivih tinti dobivenih disperzijom amfifilnih nanočestica srebra u alkoholima. Amfifilne nanočestice srebra dobivene su u dva koraka. U prvom koraku sintetizirane su poli(akrilnom kiselinom) stabilizirane nanočestice srebra redukcijom srebrovog nitrata hidrazinom. U drugom koraku provedena je modifikacija tako dobivenih nanočestica srebra reakcijom amidacije. Pripremljene su 5 % - tne suspenzije nanočestica srebra u čistom etanolu i izopropanolu. Stabilnost suspenzija provjerena je mjerenjem zeta-potencijala. Veličina pripravljenih nanočestica određena je metodom dinamičkog raspršenja svjetlosti, te je bila u rasponu od 4 do 18 nm. Pripremljena je tinta u smjesi etanola i vode u omjeru 1:1, te smjesi izopropanola i vode u omjeru 1:1. Tintama je određena površinska napetost, viskoznost i gustoća, te su ispisane na PET podlogu. Ispisanim filmovima mjeren je površinski otpor.

Sažetak (engleski)

The goal of this work is the preparation and inkjet printing of conductive inks prepared by dispersion of amphiphilic silver nanoparticles in alcohols. The synthesis of amphiphilic silver nanoparticles was performed in two steps. In the first step, silver nanoparticles were synthetized by a reduction of silver nitrate with hydrazine and poly(acrylic acid) as stabilizer. They were further modified via amidation reaction to make them amphiphilic. Silver nanoparticle suspensions (5 wt %) were prepared by dispersing the nanoparticles in ethanol and isopropyl alcohol. The stability of the suspensions was verified by measuring zeta potential. The size of the nanoparticles in the suspensions is in interval from 4 to 18 nm and was determined by using dynamic light scattering method. Finally, two inks were prepared, one in ethanol and water solution in equal volumetric ratios and second one in isopropyl alcohol and water solution in equal volumetric ratios (5 wt % nanoparticles). Surface tension, viscosity and density of the conductive inks were determined, and they were printed on PET substrate. The sheet resistance of the printed films was measured.

• Ključne riječi: amfifilne nanočestice srebra; vodljiva tinta; vodljivi filmovi; inkjet ispis; površinski otpor
• Ključne riječi (engleski): amphiphilic silver nanoparticles; conductive inks; conductive films; inkjet printing; surface resistance
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:925561
• Projekt: Šifra: UIP-2020-02-9139; Naziv: Fotonsko sinteriranje inkjet ispisanih elektrokemijskih senzora i biosenzora na plastičnim podlogama; Naziv: Photonic sintering for inkjet printed electrochemical sensors and biosensors on plastic substrates; Kratica: PrintEChemSens; Voditelj: Petar Kassal; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: UIP
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka kemijskog inženjerstva (mag. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2023-04-20 13:36:46