• Naslov (engleski): Optimizing the operation of extruders for the production of filaments
• Autor: Lucija Fiket
• Mentor: Domagoj Vrsaljko (mentor)
• Član povjerenstva: Domagoj Vrsaljko (predsjednik povjerenstva)
• Član povjerenstva: Mirela Leskovac (član povjerenstva)
• Član povjerenstva: Petar Kassal (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet kemijskog inženjerstva i tehnologije; Zagreb
• Datum i država obrane: 2018-09-17, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Kemijsko inženjerstvo; Kemijsko inženjerstvo u razvoju materijala

Sažetak

Aditivna proizvodnja u široj javnosti poznatija pod nazivom tehnologija 3D-ispisa ili „3D printanje“ je proizvodna tehnologija kod koje se materijal dodaje sloj po sloj te se time omogućava vrlo jednostavno stvaranje željenog oblika. Razvijeno je više postupaka aditivne proizvodnje, a razlikuju se u tehnologiji izrade slojeva i upotrijebljenim materijalima. Jedna od najraširenijih tehnologija je proizvodnja rastaljenim filamentom (FFF). FFF je tehnologija kojom se rastaljeni filamenti termoplastičnog materijala nanose na radnu podlogu, sloj po sloj, pomoću pokretne dizne. Da bi se dobio kvalitetan krajnji proizvod, vrlo je važno pripremiti filamente odgovarajućeg promjera. U ovom radu optimirao se proces rada ekstrudera za proizvodnju PE-HD filamenata. Eksperiment je provođen u jednopužnom ekstruderu Tin 1.1 koji ima mogućnost regulacije temperature, snage motora i brzine izvlakača. Optimiranje je provedeno u računalnom programu Design-Expert te su dobiveni optimalni uvjeti za dobivanje idealnog promjera vrijednosti 1,75 mm i minimalne standardne devijacije. Pronađeno je osam različitih kombinacija uvjeta pri kojima su dobivene željene vrijednosti promjera i male standardne devijacije. Prva kombinacija, najveće poželjnosti, daje promjer vrijednosti 1,76 mm, ima malu standardnu devijaciju koja iznosi 0,07 mm, a ostvaruje se pri temperaturi od 190 °C, snazi motora 45 % i brzini izvlakača 9 mm/s. Kako bi dobili uvid u brzinu izrade filamenata, provedena je druga analiza uz zadane kriterije: maksimalna brzina izvlakača kao najvažniji odziv, temperatura i snaga motora kao najmanje važni odzivi te promjer od 1,75 mm i minimalna standardna devijacija kao srednje važni odzivi. Optimiranjem je dobivena samo jedna kombinacija uvjeta koja daje promjer vrijednosti 1,75 mm, ima malu standardnu devijaciju koja iznosi 0,08 mm, a ostvaruje se pri temperaturi od 170 °C, snazi motora 78 % i brzini izvlakača 21 mm/s.

Sažetak (engleski)

Additive manufacturing to the wider public more commonly known as 3D-printing technology or "3D printing" is a production technology where the material is added layer by layer. Several methods of additive production have been developed. They differ in the technology for layer creation and the materials used. One of the most widespread technologies is the Fused Filament Fabrication (FFF). FFF is a technology in which the deposited thermoplastic material filaments are applied to the working surface, layer by layer, by means of a mobile nozzle. In order to obtain a quality finished product, it is very important to prepare the filaments of an appropriate diameter. In this paper the process of PE-HD filaments extrusion was optimized. The experiment was carried out in the Tin 1.1 single screw extruder, which has the ability to regulate the temperature, engine power and speed of the puller. The optimization was carried out in the Design-Expert computer program and optimal conditions were obtained for obtaining an ideal diameter of 1.75 mm and a minimum standard deviation. Eight different combinations of conditions were found in which the desired diameter values and small standard deviations were obtained. The first combination, with the highest likelihood, gives a diameter of 1.76 mm, has the smallest standard deviation of 0.07 mm and is achieved at a temperature of 190 °C, a power of 45 % and a puller speed of 9 mm/s. In order to gain insight into the speed of filament production, a second analysis was carried out with the given criteria: the maximum speed of the pullers as the most important response, the temperature and engine power as the least important responses, and diameter of 1.75 mm and minimum standard deviation as the medium-important response. By optimization, only one combination of conditions giving a 1.75 mm diameter has been obtained, it has a small standard deviation of 0.08 mm, and is achieved at a temperature of 170 °C, a power of 78 % and a pull speed of 21 mm/s.

• Ključne riječi: aditivna proizvodnja; filamenti; PE-HD; optimiranje
• Ključne riječi (engleski): additive manufacturing; filaments; PE-HD; optimizing
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:149:804173
• Projekt: Šifra: UIP-2014-09-3154; Naziv: Razvoj materijala za 3D tiskanje mikroreaktora; Naziv: Development of materials for 3D printing of microreactors; Kratica: 3Dmicroreactors; Voditelj: Domagoj Vrsaljko; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: UIP
• Studijski program: Naziv: Kemija i inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka kemijskog inženjerstva (univ. bacc. ing. cheming.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2022-05-10 11:22:05